Maraging 300 nickel bar, Maraging 300 rod, Maraging plate, Maraging 300 tube, Maraging 300 seamless pipe

Short Description:

Maraging 300/Udimar 300/Maraging C300/UNS K93120/UNS K93160
Maraging 300 alloy steels material (also referred to as Maraging C300 and Vascomax C300) is a vacuum induction melted and vacuum arc re-melted, low-carbon, nickel-cobalt-molybdenum high-temperature nickel alloy. This material can produce yield strengths in excess of 270 ksi (1862 MPa) through simple, low-temperature heat treatment at 900°F (482°C). Maraging steel 300 also exhibits good ductility at high strength levels, displays excellent notch ductility and outstanding weldability.
Maraging 300 is an age hardenable (maraging) iron nickel stainless steel. Maraging 300 has exceptional strength, toughness and is resistant to crack propagation. Maraging 300 is used for tooling, transmission shafts, autosport components and light aircraft landing gear.


Product Detail

Product Tags

Specifications

▪ UNS K93120
▪ ASTM A579
▪ AMS 6514 - Bar
▪ SAE AMS 6514 and AMS 6521 (UNS K93160) - Sheet, Strip, Plate
▪ MIL S 46850, MIL S 13881
▪ Werkstoff Nr. 1.6358 and 1.6354
▪ ASTM A579 Powder
▪ Also known as Type 300, Maraging 300, C300
▪ Vdimor 300
▪ Vascomax C300

Annealing

Maraging 300 alloy steel can be annealed at 1038°C (1900°F) after cold working and then finally cooled in air.

Cold Working

Maraging 300 alloy steel can be cold worked by conventional methods.

Welding

Maraging 300 alloy steel can be welded by conventional methods.

Forging

Maraging 300 alloy steel can be forged as for stainless 304 alloy.

Machinability

Maraging 300 alloy steel has good machinability characteristics.

Heat Treatment

Maraging 300 alloy steel cannot be heat treated for hardening except by aging.

Hot Working

Maraging 300 alloy steel can be hot worked in temperatures ranging 260 to 93°C (500 to 200°F). Age hardening takes place when this alloy steel is exposed to these temperatures for a long time.

Hardening

Maraging 300 alloy steel can be hardened by aging and cold working.

Aging

Maraging 300 alloy steel has high hardness and strength properties and is thus suitable for an aging heat treatment at 482°C (900°F).

Applications

▪ Missile & rocket motor cases
▪ Munitions
▪ Landing gear components
▪ Aerospace
▪ Extrusion tooling
▪ Die casting
▪ High performance shafting, gears & fasteners

Chemical Composition

Weight% C Si Mn S P Co Ni Mo Ti Al Fe
Maraging 300 0.03 max 0.10 max 0.10 max 0.010 max 0.010 max 8.0-9.5 18.0-19.0 4.6-5.2 0.55-0.80 0.05-0.15 Bal

Mechanical Properties

Material 0.2 % Yield Strength ksi Ultimate Tensile Strength ksi Elongation in 4D(%) Reduction of Area % Hardness HRC
Maraging 300, Solution Annealed 1500° F (816°C), 1hr, AC 120 150 16 70 30
Solution Annealed Plus Aged 900 ° F (482°C), 3 hrs AC 280 290 8 40 52